Sample - Reflow Recycled PETG - Clear and Natural Collection
Sample - Reflow Recycled PETG - Clear and Natural Collection
Want to try a colour or material first before you commit to a full roll? Here is your chance to get a 50 gram sample of it first to give it a go.
- These are off cuts from a full spool so do have a tendency to tangle. We recommend re spooling them onto an old spool.
- These spools are exposed to moisture. We recommend drying the filament out first before use.
Samples not available for discount
The Clear and Natural Collection
Reflow Natural rPLA is a bioderived material, recycled from food packaging. Our Clear rPETG’s are recycled from medical tray waste. Both are 100% recycled, without colourants or additives yet match the print performance and surface quality of the best transparent virgin materials.
100% Recycled
These streams are chosen for their consistency and quality. For users seeking the highest badge of sustainability with no compromise on quality.
Tested by the best
These 3 transparent filaments are used by some of the most pioneering 3DP designers working today in lighting, interior and furniture design.
Optimal performance
These recycled materials display excellent bed adhesion, superb print quality and stunning transparent optical quality.
Reflow is committed to sustainability as the foundation of our business. In our other filament collections we typically use 2%-5% of colourant or mattifying agent to bring beautiful colours to life. What makes this collection so special is the purity of their composition. It is a testament to the standard of recycling and production that these streams produce translucent and transparent qualities that outperform even their virgin competitors. These 3 filament types have been used in the production of high end furniture pieces and lighting collections, exhibiting their ease of printing, flawless surface finish and optimal material quality.
Transparancy
Fully Circular
Premium Print Quality
Source Traceability
PETG is another highly established plastic type, frequently used in the production of beverage and liquid containers. Reflow rPETG is sourced from a consistent stream of thermoformed medical packaging waste in the Netherlands. There are no colourants or additives of any description used in this filament collection.
A Natural Fit
Reflow is proud to be the material of choice for some of the most talented designers using 3D printing today. These clear and natural filaments have already been championed in their sustainable product lines and creations.
TECHNICAL DATA SHEET
Name : Recycled PETG
Chemical name : Polyethylene Terephthalate - Glycol Modified
Source of plastic : The Netherlands
Description : Our flagship rPETG is sourced from leading local recyclers. It’s durable and easy to use, with exceptional visual and mechanical performance
FILAMENT SPECIFICATIONS
Diameter transparent : 1.75 mm. ±0.05mm
Roundness : ≥98%
Net filament weight : 1 KG
Filament length : ~357m
PRINTER SETTING RECOMMENDATION
Nozzle temperature : 225ºC ±10ºC
Bed temperature : 75ºC ±5ºC
Bed modification : glue / hairspray
Fan speed : 30 - 100% (varies based on print geometry)
Print speed : 30 - 50 mm/s
Retraction distance : 10 mm
Retraction speed : 35-45 mm/s
Drying recommendation : 55˚C for 3 to 4 hours in a hot air or vacuum oven
MATERIAL PROPERTIES
Unit | Value | Method | |
Density | g/cm3 | 1.27 | ASTM D1505 |
Izod Impact strength | kJ/m2 | 6.2 | ISO 180 @23ºC |
Tensile stress at yield | MPa | 50 | ISO 527 |
Vicat softening temperature | ºC | 85 | ASTM D1525 |
Deflection temperature | MPa | 64 | ASTM D648 @1.82 MPa |
Elongation at yield | % | 100 | ISO 527 |
Melt flow rate (225 °C/1.20 kg) | g/10 min | 13 | ISO 1133-2 |
Glass transition | ºC | 79.2 | ISO 11357-2 |
MECHANICAL PROPERTIES
blah | Unit | Value | Method |
Tensile modulus | MPa | 1730±203 | ISO 527 |
Tensile strength | MPa | 38.4 | ISO 527 |
Tensile stress at break | MPa | 36.9 | ISO 527 |
Tensile strain at break | % | 3.3 | ISO 527 |
Flexural modulus | MPa | 1772±32 | ISO 178 |
Flexural strength | MPa | 63.6 | ISO 178 |
Flexural stress at break | MPa | 58.1 | ISO 178 |
Flexural strain at break | % | 4.2 | ISO 178 |
SAMPLE PREPARATION AND TESTING CONDITIONS
Sample preparation conditions:
Ultimaker 2+ with 0.4 mm nozzle was applied for preparing both tensile
and flexural specimens.
Line width: 0.35 mm | layer height: 0.2 mm | printing speed: 20 mm/s | retraction distance and speed: 9 mm and 35 mm/s | printing temperature: 230 ºC | fan speed: 40% | infill percentage: 100% | outline overlap: 35%
Testing conditions:
Five samples were tested and the value shared was the average value.
For tensile specimens, they were printed flatly (x-y direction ) and the printing direction
was in line with the tensile stretching direction. As for the flexural specimens, the printing direction was perpendicularly to the test direction.
DISCLAIMER
The values and recommendations provided herein are given or accepted at your own responsibility. In view of variations in maintenance or processing, neither Reflow nor its aliates provide any warranty for their use. You must make your own determination of its suitability and completeness for your specific use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products.
Shipping & Returns
Shipping & Returns
We endeavor to ship out all orders placed before 2pm on the same day during weekdays. Orders placed after our courier driver has been will be processed the following working day.
Orders placed over the weekend and public holidays are processed for shipment on the next available working day.
You will be issued with a tracking number to self monitor your shipment. Once your parcel has left our premises, there isn't any further info that we have access to aside from what shows up from your tracking number and we are unable to speed up the process.
Sorry we do not deliver to PO boxes.
Check our Refund and Returns Policy here
Disclaimer
Disclaimer
DISCLAIMER: BITS4BOTS LIMITED nor any of its Subsidiaries has any material liability (whether known or unknown, whether asserted or unasserted, whether absolute or contingent, whether accrued or unaccrued, whether liquidated or unliquidated, and whether due or to become due) arising out of any injury to individuals or property as a result of the ownership, possession or use of any product manufactured, sold, leased or delivered by BITS4BOTS LIMITED or any of its Subsidiaries